Sharpening, machining and maintaining band saw blades correctly Know how - band saws

Only professional sharpening and proper maintenance make band saws productive and effective tools in the long run. Care and maintenance of your band saw will affect its cutting quality. To achieve optimum cutting qualities, it is important to know how a band saw blade should be handled. You can see here what needs to be considered for the different methods of machining a band saw.

Types of band saw

Depending on price, there are three different types of band saw:

1. Swaged/set band saws made of CV steel (chrome vanadium steel)
2. Stellited band saws
3. Carbide-tipped band saws

Band saws are highly sensitive. If maintained incorrectly, they may break. The reason for this is that band saws are subject to a constant bending cycle. This can cause hairline cracks to form in the tooth gullet, the area of highest tensile stress.
If the saw is not resharpened on time, these cracks grow and cause breakages. To prevent this, the whole profile, i.e. all of the teeth (irrespective of their shape) of band saws made of CV steel and stellited band saws must be regularly resharpened – even when the usual degree of bluntness has not been reached in some places. Regular profile grinding can prevent premature breaking of the band saws.

If profile grinding is not carried out professionally, problematic scratches and grooves form, while excessive chip removal hardens the tooth gullet. However, with the right profile grinding machines this is not a problem.

In order to prevent saws from becoming stuck during use, you need a side projection. Therefore, band saws made of CV steel must still be set, or alternatively, swaged and levelled after profile grinding. In contrast, stellited band saws and carbide-tipped band saws require side grinding.

/// 1. Tooth face /// 2. Tooth tip /// 3. Clearance surface (tooth top) /// 4. Tooth flank /// 5. Tooth gullet

/// 1. Raw tooth /// 2. Tooth stellited into shape /// 3. Annealed and ground tooth

Stelliting refers to the process of applying Stellite® to the saw teeth and thereby hardening them. This increases the abrasion resistance of the saw cutting edges, which in turn leads to longer machine service life, increased cutting accuracy and reduced set-up times.

Stelliting is especially advantageous when particularly abrasive and hard woods are to be sawn. Stellite® no. 12 (containing 59 % Cobalt, 29 % chrome, 9 % tungsten and 1.8 % carbon) has proved to be extremely successful for machining wood. It is wear-resistant while not being too brittle, and can be ground without problems. In some cases, Stellite® no. 1 is used: This is an extremely hard alloy, which is primarily used for sawing wood with a high proportion of silicate.

In addition to painstaking manual stelliting, there are two types of machine stelliting: The resistive and the plasma welding process. During the latter, the saw tooth is heated and the required amount of stellite is melted. The liquid Stellite® is guided into forming jaws, where the raw tooth is shaped into a finished tooth. The grinding work required is therefore reduced to a minimum. In contrast to the resistive process, fully automated plasma welding has the advantage that it forms a completely solid compound layer between the Stellite® and the base material. Last but not least, repairs or replacements are cost-effective, as new Stellite® is simply applied to the existing tooth, and the costly process of grinding off leftover Stellite® is not required.

For carbide-tipped band saws, only the carbide-tipped tooth tips are ground. When doing this, the following sequence must be observed: First the tooth face, then the flank surface and then the tooth top.

Stellited saws must also be ground on the flanks after profile grinding.

Even carbide-tipped band saws require side grinding. Irrespective of which tipping your band saws have, with the right grinding machines, you can machine the flanks correctly and extremely efficiently.

Four possible grinding programs

Sharpen downwards, lift, rapid movement back
Sharpen downwards, without lifting and back
Sharpen downwards, with feed and back
Oscillation grinding with free choice of number of feeds and strokes

In order for a CV saw to be able to cut freely during machining, the saw kerf must be wider than the body. One possibility is to set the saw teeth, and therefore the alternating bending. When doing this, it must be ensured that the teeth are not set too much, otherwise the cutting quality will be reduced. However, if the teeth are not set enough, the saw heats up, develops burn marks and loses tension.

As a general rule, only the top third of the teeth should be set. However, the set width depends on various factors:

Type of wood: The softer the wood, the greater the set width
Wood moisture: The wetter the wood, the greater the set width
Resin content: The higher the resin content, the greater the set width
State of the wood: Frozen wood requires less set
Type of wood fibre: Types of wood with extremely smooth fibres require more set

Swaging saw teeth is another possibility, along with setting, for ensuring that the band saw can cut freely during machining. For the swaging process, a swaging bolt is placed in front of the saw tooth. The saw tooth is held in place with an anvil. By turning the eccentric swaging bolt, the sawing material is pushed towards the tooth tip. When the swaging process has ended, the swaging bolt turns back to its starting position.

Levelling takes place after swaging, i.e. the material which was pushed towards the tooth flanks is pressed together with the appropriate equalising jaws, so that the tooth tip is conically tapered downwards and backwards. As the swaged saw tooth works on the entire kerf width, it carries out the same work which would be carried out by two teeth on a set saw. The cutting power is increased thanks to the greater number of main and minor cutting edges. In addition, the hardness grade of the base material is increased thanks to the swaging process.

The swage must be adjusted for different types of wood in order to achieve the best possible performance.

/// 1. Anvil /// 2. Swaging bolts /// 3. Swaging curve /// 4. Equalising jaws /// 5. Saw tooth

Levelling refers to the process of eliminating irregularities (dents/bumps) in the band saw blade. This is usually carried out as the first maintenance work. After being located with a straight edge, dents can be "hammered out" using a ball or club hammer, whereby the weight of the hammer must be matched to the blade thickness.

The following guidelines apply when doing this:

Hammer weighing 1250 g for blade thicknesses ≤ 1.65 mm
Hammer weighing 1500 g for blade thicknesses > 1.65 mm

Hammers should have soft, rounded striking surfaces so that they do not leave any imprints on the band saw blades, as this could negatively impact on the service life of the blade.

Tensioning or stretching means extending the middle zone of the band saw blade. This is carried out by rolling using a rolling machine. By stretching the middle zone, the toothing side and the rear edge become shorter in relation to the middle. As a result, when fitting the saw blade to the rollers in the sawing machine, the compressive stresses are released and the saw blade forms a curve in the middle. This prevents the saw blade from shifting back and forth at the most convex contact surface of the roller.

When tensioning is carried out correctly, the blade has the following characteristics:

The tooth edge is rigid and runs especially quietly during operation.
The blade lies correctly on the rollers and withstands the stresses caused by high feed rates.
The blade is not prone to drifting. Cutting quality and accuracy is maintained thanks to correct tensioning.

During straightening, the top of the band saw receives a slightly convex bowed shape using rollers. This balances out the extension of the toothing side when the saw is used. The final grinding process for the tooth gullet also causes the tooth baseline to be extended compared with the top. The condition of the saw blade must be checked along the entire top edge.

Measuring, straightening, tensioning and levelling: What used to be a labour-intensive manual task is now possible in one clamping operation.

/// 1. Levelling /// 2. Tensioning /// 3. Straightening

Welding is required to join band saw blades or repair cracks. The ends of the saw blades must be cut exactly square beforehand, and the cut surfaces must be cleaned. When this is done, the welding seam is laid on the top of the tooth. The point to be welded is then preheated to approx. 100 °C using a heating plate. After the welding operation, the blade must again be annealed to approx. 450 °C, so that the hardened structure returns to normal and the weld bead does not tear.

The following tooth shapes are usually used for band saw blades:

Your Contact

VOLLMER WERKE Maschinenfabrik GmbH

Phone+49 7351 / 571 - 0

Emailinfo@vollmer-group.com

AddressEhinger Straße 34
88400 Biberach/Riß
Germany